Abstract: Brittle cracks were observed in the welded beam-to-column connections of steel frames during an earthquake. The crack propagation and accumulated damage to the connections can lead to fractures at much lower ductility ratios. Understanding the connections’ damage behavior during an earthquake is crucial for the design of steel moment frames in seismic areas. Nine full scale beam-to-column connections were tested under constant amplitude and variable amplitude cyclic loading. The effects of loading amplitude, loading history, and peak load on the connection damage were analyzed. The damage characters were studied and three damage evolution models were calibrated and validated based on test results. The damage mechanism was investigated and an effective plastic strain index was developed to evaluate connection damage based on a ductile fracture mechanism. A fatigue fracture mechanics-based model, for evaluating the damage process of beam-to-column connections under cyclic loading, was proposed.

钢框架梁柱节点在强震作用下的损伤性能研究

[1]Anderson, J.C., Duan, J., Xiao, Y., et al., 2002. Cyclic testing of moment connections upgraded with weld overlays. Journal of Structural Engineering, 128(4):509-516.

[2]BS (British Standards), 2005. Eurocode 3: Design of Steel Structures: Part 1-1: General Rules and Rules for Buildings, BS EN 1993-1-1. BS, London, UK.

[3]Chen, T., 2007. Extremely Low Cycle Fatigue Assessment of Thick-walled Steel Piers. PhD Thesis, Nagoya University, Japan.

[4]Chi, B., Uang, C.M., 2002. Cyclic response and design recommendations of reduced beam section moment connections with deep columns. Journal of Structural Engineering, 128(4):464-473.

[5]Dexter, R.J., Melendrez, M.I., 2000. Through-thickness properties of column flanges in welded moment connections. Journal of Structural Engineering, 126(1):24-31.

[6]El-Tawil, S., Mikesell, T., Vidarsson, E., et al., 1998. Strength and Ductility of FR Welded-bolted Connections. SAC Report No. 98-01, Washington, USA.

[7]Fisher, J.W., Dexter, R.J., Kaufmann, E.J., 1995. Fracture Mechanics of Welded Structural Steel Connections. SAC Report No. 95-09, Washington, USA.

[8]Kanvinde, A.M., Deierlein, G.G., 2004. Micromechanical Simulation of Earthquake-induced Fracture in Steel Structures. Blume Center TR 145. Stanford University, Stanford, USA.

[9]Krawinkler, H., Zhorei, M., 1983. Cumulative damage in steel structures subjected to earthquake ground motions. Computers & Structures, 14(1-4):531-541. https://doi.org/10.1016/0045-7949(83)90193-1

[10]Kuwamura, H., 1998. Fracture of steel during an earthquake– state-of-the-art in Japan. Engineering Structures, 20(4-6):310-322.

[11]Kuwamura, H., Yamamoto, K., 1997. Ductile crack as trigger of brittle fractures in steel. Journal of Structural Engineering, 123(6):729-735.

[12]Kuwamura, H., Takagi, N., 2004. Similitude law of prefracture hysteresis of steel members. Journal of Structural Engineering, 130(5):752-761.

[13]Li, H.Q., Ben, Q.G., Yu, Z.C., et al., 2004. Analysis and experiment of cumulated damage of steel frame structures under earthquake action. Journal of Building Structures, 25(3):69-74 (in Chinese).

[14]Liu, X.Y., Wang, Y.Q., Xiong, J., et al., 2016. Investigation on micromechanical fracture prediction model of high strength steel and its weld. Journal of Building Structures, 37(6):228-235 (in Chinese).

[15]MOHURD (Ministry of Housing and Urban-rural Development of the People’s Republic of China), 2003. Code for Design of Steel Structures, GB50017-2003. MOHURD, China (in Chinese).

[16]MOHURD (Ministry of Housing and Urban-rural Development of the People’s Republic of China), 2010. Code for Seismic Design of Buildings, GB50011-2010. MOHURD, China (in Chinese).

[17]Nip, K.H., Gardner, L., Davies, C.M., et al., 2010. Extremely low cycle fatigue tests on structural carbon steel and stainless steel. Journal of Constructional Steel Research, 66(1):96-110.

[18]Park, A.J., Ang, H.S., 1985. Mechanistic seismic damage model for reinforced concrete. Journal of Structure Engineering, 111(4):722-731.

[19]Rice, J.R., Tracey, D.M., 1969. On the ductile enlargement of voids in triaxial stress fields. Journal of Mechanics and Physics of Solids, 17(3):201-217.

[20]Saiprasertkit, K., Hanji, T., Miki, C., 2012. Fatigue strength assessment of load-carrying cruciform joints with material mismatching in low- and high-cycle fatigue regions based on the effective notch concept. International Journal of Fatigue, 40:120-128.

[21]Sakano, M., Wahab, M.A., 2001. Extremely low cycle (ELC) fatigue cracking behaviour in steel bridge rigid frame piers. Journal of Materials Processing Technology, 118(1-3):36-39.

[22]Shen, Z.Y., Shen, S., 2002. Seismic analysis of steel tall structures with damage cumulation and fracture effects. Journal of Tongji University, 30(4):393-398 (in Chinese).

[23]Shi, W.L., Xiao, Y., Li, G.Q., et al., 2008. Pseudo-dynamic tests on composite joints with flush end plate connections. Earthquake Engineering and Engineering Vibration, 28(6):124-133 (in Chinese).

[24]Shi, Y.J., Ao, X.L., Wang, Y.Q., et al., 2009. Experimental study on the seismic performance of beam-to-column composite connections in medium-high strength steel frame structures. China Civil Engineering Journal, 42(4):48-54 (in Chinese).

[25]Skallerud, B., Zhang, Z.L., 1997. A 3D numerical study of ductile tearing and fatigue crack growth under nominal cyclic plasticity. International Journal of Solids and Structures, 34(24):3141-3161.

[26]Solomon, H.D., 1972. Low-cycle fatigue crack-propagation in 1018 steel. Journal of Materials, 7(3):299-306.

[27]Su, D., 2005. Seismic Behavior of Beam-column Connections in Steel Structure with Composite Effect. PhD Thesis, Tsinghua University, Beijing, China (in Chinese).

[28]Tateishi, K., Hanji, T., 2004. Low cycle fatigue strength of butt-welded steel joint by means of new testing system with image technique. International Journal of Fatigue, 26(12):1349-1356.

[29]Toyoda, M., 2002. Properties of Steel Structures Damaged in Hanshin-Japan and Northridge-USA Earthquake. Seminar Notes. Dokuz Eylul University, Izmir, Turkey.

[30]Wang, J.M., Chen, L.Z., 2005. Damage detection of frames using the increment of lateral displacement change. Journal of Zhejiang University-SCIENCE A, 6(3):202-212.

[31]Wang, Y.Q., Zhou, H., Shi, Y.J., et al., 2011. Fracture prediction of welded steel connections using traditional fracture mechanics and calibrated micromechanics based models. International Journal of Steel Structures, 11(3):351-366.

[32]Xiong, J., 2011. Research on the Damage Behavior and Calculation Model of Welded Connections in Steel Frames under Earthquakes. PhD Thesis, Tsinghua University, Beijing, China (in Chinese).