PREPARATION AND CHARACTERISTICS OF NEW TYPE NANOCOMPOSITE POWDER


Author(s):  LING Guo-ping, LI Jian, WANG Shang-jun

Affiliation(s):  Department of Materials Engineering, Zhejiang University, Hangzhou 310027, China

Corresponding email(s): 

Key Words:  nanocomposite powder, Al203 nanoparticles, electroless plating enhanced with ultrasonic wave


Share this article to: More

LING Guo-ping, LI Jian, WANG Shang-jun. PREPARATION AND CHARACTERISTICS OF NEW TYPE NANOCOMPOSITE POWDER[J]. Journal of Zhejiang University Science A, 2001, 2(4): 376-378.

@article{title="PREPARATION AND CHARACTERISTICS OF NEW TYPE NANOCOMPOSITE POWDER",
author="LING Guo-ping, LI Jian, WANG Shang-jun",
journal="Journal of Zhejiang University Science A",
volume="2",
number="4",
pages="376-378",
year="2001",
publisher="Zhejiang University Press & Springer",
doi="10.1631/jzus.2001.0376"
}

%0 Journal Article
%T PREPARATION AND CHARACTERISTICS OF NEW TYPE NANOCOMPOSITE POWDER
%A LING Guo-ping
%A LI Jian
%A WANG Shang-jun
%J Journal of Zhejiang University SCIENCE A
%V 2
%N 4
%P 376-378
%@ 1869-1951
%D 2001
%I Zhejiang University Press & Springer
%DOI 10.1631/jzus.2001.0376

TY - JOUR
T1 - PREPARATION AND CHARACTERISTICS OF NEW TYPE NANOCOMPOSITE POWDER
A1 - LING Guo-ping
A1 - LI Jian
A1 - WANG Shang-jun
J0 - Journal of Zhejiang University Science A
VL - 2
IS - 4
SP - 376
EP - 378
%@ 1869-1951
Y1 - 2001
PB - Zhejiang University Press & Springer
ER -
DOI - 10.1631/jzus.2001.0376


Abstract: 
This new type nanocomposite powder was prepared with electroless plating enhanced by ultrasonic wave. High-resolution transmission electron microscopy (HRTEM) showed that As-plated particles have nano meter scale average size. X-ray diffraction (XRD) analysis showed the presence of a noncrystalline structure in the plating layer on the nano-Al2O3 matrix. The content of the plating layer was analyzed by energy disper sive X-ray spectroscopy (EDX) technology. The plating layer content was adjustable by changing the solution concentration.

Darkslateblue:Affiliate; Royal Blue:Author; Turquoise:Article

Reference

[1] Chen, D. J., Mayo, M. J., 1996. Rapid rate sintering of nanocrystalline ZrO2 minus 3 mol% Y2O3. J. Am. Ceram. Soc., 79(4):906-912.

[2] Li,H. Q., Liu, J. B., 1998. Low temperature electroless nickel plating by use of ultrasonic wave. Plating and Polish, 17(3):14-17(in Chinese).

[3] Li,J., Mao, D.S., 1997. A new kind of cermet and its wear resistance. Letter of advanced technology, 7 (7):15-2O.

[4] Li,Y. K., Guo, L., 1995. Studies of fracture behavior on nano-A12O3 and A12O3-based nanocomposite ceramics. J. Jilin Arboriculture College, 11(3):155-159 (in Chinese).

[5] Mao, D. S., Li, J., Guo, S.Y. et al., 1997. Study of abrasion behavior of an advanced A12O3-TiC-Co ceramic. Wear, 209(1):153-159.

[6] Mao,D.S., Liu,X. H., Li,J. et al., 1998. Fine cobalttoughened A12O3-TiC ceramic and its wear resistance.J. Mate. Sci., 33(23):5677-5682.

[7] Ni,Y.H., Ge, X.W., Xu,X.L. et al., 2000. Developments in preparation of nano-scale materials. J. Inorganic Mater., 15(1):9-15(in Chinese).

[8] Wu,S.J., De,J., Lutgard, C. et al., 1996. Sintering of nanophase gamna-A12O3 powder. J. Am. Ceram. Soc., 79(8):2207-2211.

[9] Zhang, L. D., 1993. Nanomaterials. Science Press, Beijing. p.54(in Chinese).

Open peer comments: Debate/Discuss/Question/Opinion

<1>

Please provide your name, email address and a comment





Journal of Zhejiang University-SCIENCE, 38 Zheda Road, Hangzhou 310027, China
Tel: +86-571-87952783; E-mail: cjzhang@zju.edu.cn
Copyright © 2000 - 2024 Journal of Zhejiang University-SCIENCE